| TYPICAL PROPERTIES (1) | | | |
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 110 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 90 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 7 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 60 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3580 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 173 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3430 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 105 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 85 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 60 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3200 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 160 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3300 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1335 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 53 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 55 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 0 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 6 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 218 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 201 | °C | ASTM D 648 |
| CTE, -20°C to 150°C, flow | 5.58E-05 | 1/°C | ASTM E 831 |
| CTE, -20°C to 150°C, xflow | 5.4E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 5.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 215 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 211 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 215 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 170 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 170 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 170 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.27 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 337°C/6.6 kgf | 9 | g/10 min | ASTM D 1238 |
| Density | 1.27 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 1.25 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.7 | % | ISO 62 |
| Melt Volume Rate, MVR at 220°C/5.0 kg | 13 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+17 | Ohm-cm | ASTM D 257 |
| Dielectric Strength, in air, 1.6 mm | 32.7 | kV/mm | ASTM D 149 |
| Dielectric Strength, in oil, 1.6 mm | 27.9 | kV/mm | ASTM D 149 |
| Relative Permittivity, 1 kHz | 3.15 | - | ASTM D 150 |
| Dissipation Factor, 1 kHz | 0.0013 | - | ASTM D 150 |
| Dissipation Factor, 2450 MHz | 0.0025 | - | ASTM D 150 |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 |
| Hot Wire Ignition {PLC) | 1 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 2 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 3 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-2 Flame Class Rating (3) | 0.4 | mm | UL 94 |
| UL Recognized, 94V-1 Flame Class Rating (3) | 0.75 | mm | UL 94 |
| UL Recognized, 94V-0 Flame Class Rating (3) | 0.75 | mm | UL 94 |
| UL Recognized, 94-5VA Rating (3) | 3 | mm | UL 94 |
| Oxygen Index (LOI) | 47 | % | ASTM D 2863 |
| NBS Smoke Density, Flaming, Ds 4 min | 0.7 | - | ASTM E 662 |
| Source GMD, last updated:11/02/2007 | | |